Insulation Self-Adhesive Fiberglass Banding Tape

• Application: Insulators, Electrical Winding Insulation, Winding Wire Coating Insulation, Electrical Base, Shell, Motor, Switch Baseplate
• Type: Solid
• Chemistry: Inorganic Insulation
• Material: Glass Fiber
• Thermal Rating: F 155
• Maximum Voltage: 10KV~20KV
• Model NO.: LT-PGW
• Classification: Inorganic Insulation Material
• Certification: ISO9001
• Color: White
• Raw Material: E-Glass Yarns + Polyester Resin
• Thermal Grade: F, H Grade
• Thickness: 0.17mm, 0.30mm
• Width: 10,15, 20, 25, 30, 32, 40, 50mm
• Curing Condition: 150°c, 2 Hours
• Length/Roll: 100,150, 200 Meters
• Storage Temperature: Room Temperature
• Appliaction: Oil Transformer, Motor and Rotor
• Lead Time: 10~20 Days
• Transport Package: Roll
• Trademark: LONTOM
• Origin: Shanghai, China
• HS Code: 70199000
• Production Capacity: 50, 000 Roll Per Month

Product Description

Fiber Glass Banding Tape
1.Thickness:0.2~0.5mm
2.Fiberglass banding tape
3.Self-adhesive insulation tape
4.SGS,RoHS

The banding tapes are of high quality, which consist of parallel twisted E-glass yarns preimpregnated with a special thermosetting polyester resin and manufactured with the proprietory technology and advanced equipments.

Specification :

Type	Width (mm)	Thickness (mm)	Put up
H grade F grade	10.20.25.30.50±10%	0.30±10%	Spool or pancake

 

Technical Data:

Test content	Unit	Standard Value
Thermal class		H grade	F grade
Volatile content	%	not above : 2
Loss of weight at calcination	%	26±2
Soluble resin content	%	above : 90
Tensile strength before curing	N/cm	above :1500	above :1000
Maximum pull while banding	N/cm	800	800
Tensile strength of ringlike sample at room temperature after curing	Mpa	20°C
		above :900	above :900
Tensile strength of ringlike sample at working temperature after curing	Mpa	180°C	150°C
		above :600	above :560
Proof tracking index		above 500V
Arc resistance	S	above : 160
Breakdown voltage parallel to layers	KV	normal condition:adove 25 after soaked in water for 24 hours:above 10
Thermosetting	OK
Loss of tensile strength after soaked in oil	not above:10%

 

Curing condition (Time to bring the piece to the temperature is not considered)

Temperature	°C	160	150	135	120	115
Time	hour	2.5	3.0	5.0	14.0	20.0

  

Storage Stability:

Storage temperature		°C	10	15	20	30
Time	H grade	month	24	18	12	8
	F grade		20	15	10	6