Impregnated Glass Fiber Web Banding Tape (PGW)

• Application: Electrical Winding Insulation, Winding Wire Coating Insulation, Electrical Base, Shell, Motor
• Type: Solid
• Chemistry: Inorganic Insulation
• Material: Fiberglass
• Thermal Rating: H 180
• Maximum Voltage: 20KV~100KV
• Model NO.: LT-PGW
• Classification: Inorganic Insulation Material
• Certification: ISO9001
• Color: White
• Brand: Lontom
• Thickness: 0.17~0.33mm
• Thermal Grade: B, F, H Grade
• Raw Material: Fiber Glass + Unsaturated Polyester Resin
• Transport Package: Spool
• Trademark: LONTOM
• Origin: Shanghai, China
• HS Code: 70199000
• Production Capacity: 5, 000, 000 Meters Yearly

Product Description

Edge banding tape
1. Thickness: 0.17~0.33mm
2. Tensile strength: 2000N/cm
3. Thermal Grade: B, F, H
4. SGS, RoHS, adhesive tape

The banding tapes are of high quality, which consist of parallel twisted E-glass yarns preimpregnated with a special thermosetting polyester resin, and manufactured with the proprietory technology which are transferred from VONROLL ISOLA of Italy.

It's widely used in AC. DC motors, generators and transformers especially in traction motors.

		H200-W	H200-G-W	F150-G-W
Thermal class		H		F
Volatile content	%	not above: 2
Loss of weight at calcination	%	26± 2
Soluble resin content	%	above: 90
Tensile strength before curing	N/cm	above: 2000	above: 1500	above: 1000
Maximum pull while banding	N/cm	1000	800	800
Tensilestrength of ringlike sample at room temperature after curing	Mpa	200c
		above: 1000	above: 900	above: 900
Tensile strength of ringlike sample at working temperature after curing	Mpa	2000c	1800c	1500c
		above: 700	above: 600	above: 560
Proof tracking index		above 500V
Arc resistance	S	above: 160
Breakdown voltage parallel to layers	KV	normal condition: adove 25
		after soaked in water for 24
		hours: above 10
Thermosetting	OK
Loss of tensile strength after soaked in oil	not above: 10%